STUDY ON DURABILITY OF CFRP SUBJECTED TO FREEZE-THAW CYCLE COMBINED WITH SUSTAINED LOAD

More Information
  • Received Date: December 31, 1899
  • Revised Date: December 31, 1899
  • Carbon Fiber-Reinforced Polymer (CFRP) material is increasingly being used for the retrofit and repair of concrete structures. However, there is insufficient information on the environmental durability of CFRP, especially under aggravating environmental conditionings combined with sustained loads. The coupled effects of freeze-thaw cycle and sustained loads on the long term behaviour of CFRP were investigated. The CFRP specimens are subjected to freeze-thaw cycle in an unstressed state or loaded in about 30% or 60% of the initial ultimate load, and there involve, respectively, 50, 100, 200 and 300 times of freeze-thaw cycles in water solution. The ultimate strength, elongation and elastic modulus of CFRP are studied after coupled actions of freeze-thaw cycle and sustained loads. The test results indicate that the coupled action of a freeze-thaw cycle and a sustained load had an effect on ultimate strength and elongation of specimen, while did not have any significant effect on elastic modulus of specimen. A simple residual strength damage model of CFRP under a freeze-thaw cycle and a sustained load is presented.
  • Related Articles

    [1]XIAO Xiong, WANG Ze-yu, LI Quan-wang, CAO Mai. BAYESIAN MODEL UPDATING BASED ON STRUCTURAL RELIABILITY METHOD: CASE STUDY FOR CHLORIDE-INDUCED DURABILITY ANALYSIS[J]. Engineering Mechanics, 2022, 39(S): 336-341. DOI: 10.6052/j.issn.1000-4750.2021.07.S060
    [2]GU Hui, LI Quan-wang, HOU Guan-jie. UPDATING METHOD FOR DURABILITY MODELS OF CONCRETE STRUCTURES IN CARBONATION ENVIRONMENT[J]. Engineering Mechanics, 2021, 38(5): 113-121. DOI: 10.6052/j.issn.1000-4750.2020.06.0361
    [3]PANG Long, YING Zong-quan, FAN Zhi-hong, TIAN Jun-feng, LI Quan-wang. ENVIRONMENTAL LOAD MODEL AND DURABILITY ANALYSIS OF MARINE CONCRETE STRUCTURES BASED ON IN-SITU TEST DATA IN SOUTH CHINA[J]. Engineering Mechanics, 2016, 33(增刊): 168-172. DOI: 10.6052/j.issn.1000-4750.2015.04.S019
    [4]ZHAO Wei-tao, ZHANG Xu. COMBINED ANALYSIS METHOD FOR STRUCTURAL DURABILITY AND DAMAGE TOLERANCE BASED ON THRESHOLD BEYOND PROBABILITY[J]. Engineering Mechanics, 2011, 28(10): 52-057.
    [5]GAN Wei-zhong, JIN Wei-liang, RAUPACH M. THE IN-SITU MONITORING PRINCIPLES AND THE RESIDUAL LIFE PREDICTION OF THE DURABILITY OF CONCRETE STRUCTURE IN MARINE ENVIRONMENT[J]. Engineering Mechanics, 2011, 28(增刊Ⅱ): 78-84,9.
    [6]JIN Wei-liang, NIU Di-tao. THE STATE-OF-THE-ART ON DURABILITY AND LIFE-CYCLE DESIGN THEORY OF ENGINEERING STRUCTURES[J]. Engineering Mechanics, 2011, 28(增刊Ⅱ): 31-37.
    [7]SHI Yang-hang, WANG Dan-fang, WU Ze-jin. DURABILITY PROTECTION OF SAND CONCRETE[J]. Engineering Mechanics, 2010, 27(增刊Ⅱ): 212-216.
    [8]PAN Hong-ke, NIU Ji-shou, YANG Lin-de, TANG Yong-jing. THE DURABILITY DETERIORATION MODEL BASED ON CARBONATION FOR UNDERGROUND CONCRETE STRUCTURES[J]. Engineering Mechanics, 2008, 25(7): 172-178.
    [9]HE Xiao-fan, LIU Wen-ting, XIANG Jin-wu. PROBABILISTIC FRACTURE MECHANICS APPROACH FOR DURABILITY ANALYSIS ON PRE-CORROSION STRUCTURES[J]. Engineering Mechanics, 2008, 25(5): 39-044.
    [10]LIU Jian-fei, CHEN Wei-hong, CHENG Zhao-xia. INFLUENTIAL FACTORS ANALYSIS ON DURABILITY OF CONCRETE STRUCTURES IN COAL MINE AREA[J]. Engineering Mechanics, 2007, 24(增Ⅰ): 129-133.

Catalog

    Article Metrics

    Article views (1392) PDF downloads (525) Cited by()
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return