碱激发矿粉海水海砂混凝土与CFRP筋粘结性能研究

徐金金 杨树桐 刘治宁

徐金金, 杨树桐, 刘治宁. 碱激发矿粉海水海砂混凝土与CFRP筋粘结性能研究[J]. 工程力学, 2019, 36(S1): 175-183. doi: 10.6052/j.issn.1000-4750.2018.05.S036
引用本文: 徐金金, 杨树桐, 刘治宁. 碱激发矿粉海水海砂混凝土与CFRP筋粘结性能研究[J]. 工程力学, 2019, 36(S1): 175-183. doi: 10.6052/j.issn.1000-4750.2018.05.S036
XU Jin-jin, YANG Shu-tong, LIU Zhi-ning. STUDY ON THE BOND PERFORMANCE BETWEEN CFRP BARS AND ALKALI-ACTIVATED SLAG SEAWATER AND SEA SAND CONCRETE[J]. Engineering Mechanics, 2019, 36(S1): 175-183. doi: 10.6052/j.issn.1000-4750.2018.05.S036
Citation: XU Jin-jin, YANG Shu-tong, LIU Zhi-ning. STUDY ON THE BOND PERFORMANCE BETWEEN CFRP BARS AND ALKALI-ACTIVATED SLAG SEAWATER AND SEA SAND CONCRETE[J]. Engineering Mechanics, 2019, 36(S1): 175-183. doi: 10.6052/j.issn.1000-4750.2018.05.S036

碱激发矿粉海水海砂混凝土与CFRP筋粘结性能研究

doi: 10.6052/j.issn.1000-4750.2018.05.S036
基金项目: 国家自然科学基金项目(51778591)
详细信息
    作者简介:

    徐金金(1994-),女,山东人,硕士生,主要从事碱激发混凝土力学性能研究(E-mail:1311996541@qq.com);刘治宁(1984-),男,山东人,中级建筑材料本科,材料检测员,主要从事混凝土鉴定检测工作(E-mail:38778557@qq.com).

    通讯作者: 杨树桐(1979-),男,山东人,教授,博士,主要从事混凝土断裂力学、新型混凝土材料的理论与试验研究(E-mail:shutongyang2013@163.com).
  • 中图分类号: TU377.9+4

STUDY ON THE BOND PERFORMANCE BETWEEN CFRP BARS AND ALKALI-ACTIVATED SLAG SEAWATER AND SEA SAND CONCRETE

  • 摘要: 该文通过试验分析研究了碱激发矿粉海水海砂混凝土与碳纤维筋(Carbon Fiber Reinforced Polymer)筋的粘结性能。分别考虑了碱激发矿粉淡水河砂混凝土(FRASC)、碱激发矿粉淡水海砂混凝土(FSASC)、碱激发矿粉海水河砂混凝土(SRASC)和碱激发矿粉海水海砂混凝土(SSASC)四种碱激发矿粉混凝土(ASC),并与钢筋的粘结性能进行了对比。试验中分别采用直径为8 mm的CFRP筋和HRB400带肋钢筋,粘长分别为2.5 d、5 d、7.5 d、10 d和15 dd为筋的直径)。结果表明:粘长为15 d的试件,CFRP筋的试件全部劈裂破坏,钢筋粘长为10 d、15 d的试件全部为钢筋拉断破坏;粘长为2.5 d的CFRP筋试件将筋表面的脱模带拉断而出现第二个峰值;粘结滑移曲线可分为微滑移阶段、滑移阶段、剥离阶段、软化阶段和残余阶段。
  • [1] 史才军, 巴维尔·克利文科, 黛拉·罗伊. 碱-激发水泥和混凝土[M]. 北京:化学工业出版社, 2006. Shi Caijun, Krivenko P, Roy D. Alkali-activated cements and concretes[M]. Beijing:Chemical Industry Press, 2006. (in Chinese)
    [2] Wang S D, Scrivener K L. Hydration products of alkali activated slag cement[J]. Cement and Concrete Research, 1995, 25(3):561-571.
    [3] Yang C H, Wu F, Chen K. Research on set retarder of high and super high strength alkali -activated slag cement and concrete[J]. Key Engineering Materials, 2011, 477:164-169.
    [4] Bilek V, Hurta J, Done P, et al. Development of alkali-activated concrete for structures-Mechanical properties and durability[J]. Perspectives in Science, 2016, 7:190-194.
    [5] Zhang J, Shi C J, Zhang Z H, et al. Durability of alkali-activated materials in aggressive environments:A review on recent studies[J]. Construction and Building Materials, 2017, 152:598-613.
    [6] 姜正平, 明维. 碱激发矿渣蒸压混凝土中钢筋早期锈蚀状况[J]. 建筑材料学报, 2016, 21(2):222-227. Jiang Zhengping, Ming Wei. Early corrosion behavior of steel bars embedded in the autoclave cured alkaliactivated slag concrete[J]. Journal of Building Materials, 2016, 21(2):222-227. (in Chinese)
    [7] 施锦杰, 邓晨皓, 张亚梅. 钢筋在碱激发矿渣砂浆中的早起腐蚀行为[J]. 建筑材料学报, 2016, 19(6):969-975. Shi Jinjie, Deng Chenhao, Zhang Yamei. Early corrosion behavior of rebars enbedded in the alkali-activated slag mortar[J]. Journal of Building Materials, 2016, 19(6):969-975. (in Chinese)
    [8] Li Y L, Zhao X L, Raman Singh R K, et al. Thermal and mechanical properties of alkali-activated slag paste, mortar and concrete utilising seawater and sea sand[J]. Construction and Building Materials, 2018, 159:704-724.
    [9] Ravikumar D, Neithalath N. Electrically induced chloride ion transport in alkali activated slag concretes and the influence of microstructure[J]. Cement and Concrete Research, 2013, 47(5):31-42.
    [10] Li Y L, Zhao X L, Raman Singh R K, et al. Experimental study on seawater and sea sand concrete filled GFRP and stainless steel tubular stub columns[J]. Thin-Walled Structures, 2016, 106:390-406.
    [11] Li Y L, Zhao X L, Raman Singh R K, et al. Tests on seawater and sea sand concrete-filled CFRP, BFRP and stainless steel tubular stub columns[J]. Thin-Walled Structures, 2016, 108:163-184.
    [12] Wang Z, Zhao X L, Xian G, et al, Durability study on interlaminar shear behaviour of basalt-, glass- and carbon-fibre reinforced polymer (B/G/CFRP) bars in sea water sea sand concrete environment[J]. Construction and Building Materials, 2017, 156:985-1004.
    [13] Wang Z, Zhao X L, Xian G, et al. Long-term durability of basalt-and glass-fibre reinforced polymer (BFRP/GFRP) bars in seawater and sea sand concrete environment[J]. Construction and Building Materials, 2017, 139:467-487.
    [14] Castel A, Foster S J. Bond strength between blended slag and Class F fly ash geopolymer concrete with steel reinforcement[J]. Cement and Concrete Research, 2015, 72:48-53.
    [15] Bilek V, Bonczková S, Hurta J, et al. Bond strength between reinforcing steel and different types of concrete[J]. Procedia Engineering, 2017, 190:243-247.
    [16] Laskar S M, Talukdar S. Preparation and tests for workability, compressive and bond strength of ultra-fine slag based geopolymer as concrete repairing agent[J]. Construction and Building Materials, 2017, 154:176-190.
    [17] Tekle B H, Khennane A, Kayali O. Bond behaviour of GFRP reinforcement in alkali activated cement concrete[J]. Construction and Building Materials, 2017, 154:972-982.
    [18] Tekle B H, Khennane A, Kayali O. Bond of spliced GFRP reinforcement bars in alkali activated cement concrete[J]. Engineering Structures, 2017, 147:740-751.
  • [1] 薛建阳, 董金爽, 隋龑, 刘祖强.  附设粘滞阻尼器的传统风格建筑混凝土双枋-柱节点抗震性能分析 . 工程力学, 2018, 35(1): 98-108. doi: 10.6052/j.issn.1000-4750.2016.08.0606
    [2] 陈俊, 张白, 杨鸥, 蒋恩浩.  微锈蚀钢筋混凝土高温后粘结锚固性能试验研究 . 工程力学, 2018, 35(10): 92-100. doi: 10.6052/j.issn.1000-4750.2017.06.0491
    [3] 杨超, 杨树桐, 戚德海.  BFRP筋与珊瑚混凝土粘结性能试验研究 . 工程力学, 2018, 35(S1): 172-180. doi: 10.6052/j.issn.1000-4750.2017.06.S034
    [4] 曹芙波, 唐磊杰, 丁兵兵, 王晨霞.  冻融损伤后钢筋与再生混凝土黏结滑移性能试验研究 . 工程力学, 2017, 34(增刊): 244-251. doi: 10.6052/j.issn.1000-4750.2016.04.S050
    [5] 郭诗惠, 孔搏, 蔡春声, 张建仁, 曾学.  GFRP-混凝土组合板界面抗剪连接性能的试验研究 . 工程力学, 2017, 34(2): 216-225. doi: 10.6052/j.issn.1000-4750.2016.04.0285
    [6] 牛建刚, 郝吉, 孙立斌, 李伯潇.  塑钢纤维轻骨料混凝土与钢筋粘结锚固试验研究 . 工程力学, 2017, 34(2): 42-49. doi: 10.6052/j.issn.1000-4750.2016.05.ST05
    [7] 巨玉文, 梁仁旺, 白晓红, 张善元.  挤扩支盘桩中支盘破坏形态的试验研究 . 工程力学, 2013, 30(5): 188-194. doi: 10.6052/j.issn.1000-4750.2012.01.0041
    [8] 王博, 白国良, 代慧娟, 吴淑海.  再生混凝土与钢筋粘结滑移性能的试验研究及力学分析 . 工程力学, 2013, 30(10): 54-64. doi: 10.6052/j.issn.1000-4750.2012.06.0396
    [9] 郑建岚, 庄金平.  自密实混凝土与钢筋的粘结性能试验研究 . 工程力学, 2013, 30(2): 112-117. doi: 10.6052/j.issn.1000-4750.2011.08.0530
    [10] 周乐, 王晓初, 刘洪涛.  碳纤维混凝土力学性能与破坏形态试验研究 . 工程力学, 2013, 30(增刊): 226-231. doi: 10.6052/j.issn.1000-4750.2012.04.S066
    [11] 原海燕, 安明喆, 贾方方, 余自若.  活性粉末混凝土轴拉性能试验研究 . 工程力学, 2011, 28(增刊I): 141-144.
    [12] 刘卫东, 林瑜, 钟海荣, 苏海华.  抗冲刷磨蚀混凝土的耐磨损试验研究 . 工程力学, 2011, 28(增刊Ⅱ): 157-160,.
    [13] 李会杰, 谢 剑.  超低温环境下钢筋与混凝土的粘结性能 . 工程力学, 2011, 28(增刊I): 80-084.
    [14] 申玉生;高 波;王峥峥.  强震区山岭隧道振动台模型试验破坏形态分析 . 工程力学, 2009, 26(增刊 I): 62-066.
    [15] 张国军;杜晓琴;刘建新;王红囡.  高轴压比高强混凝土足尺框架柱的破坏形态分析 . 工程力学, 2009, 26(增刊 I): 89-093.
    [16] 杨 勇, 谢标云, 聂建国, 周丕健.  表层嵌贴碳纤维筋加固钢筋混凝土梁受力性能试验研究 . 工程力学, 2009, 26(3): 106-112.
    [17] 徐世烺, 王洪昌.  超高韧性水泥基复合材料与钢筋粘结本构关系的试验研究 . 工程力学, 2008, 25(11): 53-061.
    [18] 郝庆多, 王言磊, 侯吉林, 欧进萍.  GFRP带肋筋粘结性能试验研究 . 工程力学, 2008, 25(10): 0-165,.
    [19] 李忠献.  钢筋混凝土分体柱理论与技术 . 工程力学, 2005, 22(S1): 127-141.
    [20] 郑山锁, 邓国专, 杨勇, 俞茂宏, 张俊峰.  型钢混凝土结构粘结滑移性能试验研究 . 工程力学, 2003, 20(5): 63-69.
  • 加载中
计量
  • 文章访问数:  50
  • HTML全文浏览量:  0
  • PDF下载量:  11
  • 被引次数: 0
出版历程
  • 收稿日期:  2018-05-02
  • 修回日期:  2018-11-23
  • 刊出日期:  2019-06-30

碱激发矿粉海水海砂混凝土与CFRP筋粘结性能研究

doi: 10.6052/j.issn.1000-4750.2018.05.S036
    基金项目:  国家自然科学基金项目(51778591)
    作者简介:

    徐金金(1994-),女,山东人,硕士生,主要从事碱激发混凝土力学性能研究(E-mail:1311996541@qq.com);刘治宁(1984-),男,山东人,中级建筑材料本科,材料检测员,主要从事混凝土鉴定检测工作(E-mail:38778557@qq.com).

    通讯作者: 杨树桐(1979-),男,山东人,教授,博士,主要从事混凝土断裂力学、新型混凝土材料的理论与试验研究(E-mail:shutongyang2013@163.com).
  • 中图分类号: TU377.9+4

摘要: 该文通过试验分析研究了碱激发矿粉海水海砂混凝土与碳纤维筋(Carbon Fiber Reinforced Polymer)筋的粘结性能。分别考虑了碱激发矿粉淡水河砂混凝土(FRASC)、碱激发矿粉淡水海砂混凝土(FSASC)、碱激发矿粉海水河砂混凝土(SRASC)和碱激发矿粉海水海砂混凝土(SSASC)四种碱激发矿粉混凝土(ASC),并与钢筋的粘结性能进行了对比。试验中分别采用直径为8 mm的CFRP筋和HRB400带肋钢筋,粘长分别为2.5 d、5 d、7.5 d、10 d和15 dd为筋的直径)。结果表明:粘长为15 d的试件,CFRP筋的试件全部劈裂破坏,钢筋粘长为10 d、15 d的试件全部为钢筋拉断破坏;粘长为2.5 d的CFRP筋试件将筋表面的脱模带拉断而出现第二个峰值;粘结滑移曲线可分为微滑移阶段、滑移阶段、剥离阶段、软化阶段和残余阶段。

English Abstract

徐金金, 杨树桐, 刘治宁. 碱激发矿粉海水海砂混凝土与CFRP筋粘结性能研究[J]. 工程力学, 2019, 36(S1): 175-183. doi: 10.6052/j.issn.1000-4750.2018.05.S036
引用本文: 徐金金, 杨树桐, 刘治宁. 碱激发矿粉海水海砂混凝土与CFRP筋粘结性能研究[J]. 工程力学, 2019, 36(S1): 175-183. doi: 10.6052/j.issn.1000-4750.2018.05.S036
XU Jin-jin, YANG Shu-tong, LIU Zhi-ning. STUDY ON THE BOND PERFORMANCE BETWEEN CFRP BARS AND ALKALI-ACTIVATED SLAG SEAWATER AND SEA SAND CONCRETE[J]. Engineering Mechanics, 2019, 36(S1): 175-183. doi: 10.6052/j.issn.1000-4750.2018.05.S036
Citation: XU Jin-jin, YANG Shu-tong, LIU Zhi-ning. STUDY ON THE BOND PERFORMANCE BETWEEN CFRP BARS AND ALKALI-ACTIVATED SLAG SEAWATER AND SEA SAND CONCRETE[J]. Engineering Mechanics, 2019, 36(S1): 175-183. doi: 10.6052/j.issn.1000-4750.2018.05.S036
参考文献 (18)

目录

    /

    返回文章
    返回